Product

Solar Encapsulant Film PO8510W

• Conformable and flexible for easy lamination
• Durable bonding strength with both glass and backsheet
• Excellent UV and damp-heat stability
• Low shrinkage rate
• High light reflection
• No acetic acid/No corrosion
• 1/10th MVTR vs. EVA
• Good compatibility with CIGS Modules

You can always contact us by phone or email, or submit your request to us.

Telephone:+86-21-54265599

Email:sales@zxchem.com.cn

  • *
  • *
  • *
  • Send
  • Specifications
  • Details
  • Download

Solar Encapsulant Film PO8510W offers protection against UV aging and weathering

– while enabling maximum light reflectivity to increase power efficiency of PV module.

Suitable for both Glass/Backsheet and Glass/Glass modules.

Items

 

Units

Type Value

Test Method

Unit Weight

 

g/m2

360-460

ASTM D882

 

Tensile (Cured)

MD

MPa

6.5

Tensile (Cured)

TD

MPa

5.0

Elongation (Cured)

 

MD

%

50

Elongation (Cured)

 

TD

%

55

Adhesion to Glass

 

N/cm

70

ASTM D903

Volume Resistivity (Cured)

 

Ω·cm

2.0×1014

ASTM D257

Reflectivity

 

%

90

ASTM 97

Dimensional Stability

(Uncured, 120 oC 3min)

MD

%

-2.2

ASTM 1204

TD

%

0.8

UV Resistance(32kWh/m2)

△b*

-

1.0

ASTM G154


Suggested Lamination Conditions

 

Condition

 

Suggested Value

 

Lamination Temperature

 

148-160oC

 

Evacuation Time

 

5-12 min

 

Press Time

 

15-18 min


Click below to download the COA of our product


ZXCHEM-Solar Encapsulant Film PO8510W